The first MALHs to be synthesized were the methylammonium derivatives [CH3NH3]SnX3 and [CH3NH3]PbX3. Their potential in the area of energy conversion wasn't realized until decades later.[8]In the [CH3NH3]PbX3cubic crystal structure the methylammonium cation ([CH3NH3]+) is surrounded by PbX6 octahedra. The X ions are not fixed and can migrate through the crystal with an activation energy of 0.6 eV; the migration is vacancy assisted.[1] The methylammonium cations can rotate within their cages. At room temperature the ions have the CN axis aligned towards the face directions of the unit cells and the molecules randomly change to another of the six face directions on a 3 ps time scale.[9]
The solubility of MALHs strongly decreases with increased temperature: from 0.8 g/mL at 20 °C to 0.3 g/mL at 80 °C for [CH3NH3]PbBr3 in dimethylformamide. This property is used in the growth of MALH single crystals and films from solution, using a mixture of [CH3NH3]X and PbX2 powders as the precursor. The growth rates are 3–20 mm3/hour for [CH3NH3]PbI3 and reach 38 mm3/hour for [CH3NH3]PbBr3 crystals.[7]
The resulting crystals are metastable and dissolve in the growth solution when cooled to room temperature. They have bandgaps of 2.18 eV for [CH3NH3]PbBr3 and 1.51 eV for [CH3NH3]PbI3, while their respective carrier mobilities are 24 and 67 cm2/(V·s).[7] Their thermal conductivity is exceptionally low, ~0.5 W/(K·m) at room temperature for [CH3NH3]PbI3.[10]
Thermal decomposition of [CH3NH3]PbI3 gives methyl iodide (CH3I) and ammonia (NH3).[11][12]
Weber, Dieter (1978). "CH3NH3SnBrxI3-x (x = 0-3), ein Sn(II)-System mit kubischer Perowskitstruktur / CH3NH3SnBrxI3-x (x = 0-3), a Sn(II)-System with Cubic Perovskite Structure". Zeitschrift für Naturforschung B. 33 (8): 862–865. doi:10.1515/znb-1978-0809. ISSN 1865-7117.
Weber, Dieter (1978-12-01). "CH3NH3PbX3, ein Pb(II)-System mit kubischer Perowskitstruktur / CH3NH3PbX3 , a Pb(II)-System with Cubic Perovskite Structure". Zeitschrift für Naturforschung B. 33 (12): 1443–1445. doi:10.1515/znb-1978-1214. ISSN 1865-7117. S2CID 93597007.*Grätzel, Michael (2014). "The light and shade of perovskite solar cells". Nature Materials. 13 (9): 838–842. Bibcode:2014NatMa..13..838G. doi:10.1038/nmat4065. ISSN 1476-1122. PMID 25141800.
Wikimedia Commons has media related to Methylammonium lead halides.
^ a bEames, Christopher; Frost, Jarvist M.; Barnes, Piers R. F.; o'Regan, Brian C.; Walsh, Aron; Islam, M. Saiful (2015). "Ionic transport in hybrid lead iodide perovskite solar cells". Nature Communications. 6: 7497. Bibcode:2015NatCo...6.7497E. doi:10.1038/ncomms8497. PMC 4491179. PMID 26105623.
^Kojima, Akihiro; Teshima, Kenjiro; Shirai, Yasuo; Miyasaka, Tsutomu (2009-05-06). "Organometal Halide Perovskites as Visible-Light Sensitizers for Photovoltaic Cells". Journal of the American Chemical Society. 131 (17): 6050–6051. doi:10.1021/ja809598r. ISSN 0002-7863. PMID 19366264.
^Náfrádi, Bálint (October 16, 2015). "Methylammonium Lead Iodide for Efficient X-ray Energy Conversion". J. Phys. Chem. C. 2015 (119): 25204–25208. doi:10.1021/acs.jpcc.5b07876.
^ a bYakunin, S.; Dirin, D.; Shynkarenko, Y.; Morad, V.; Cherniukh, I.; Nazarenko, O.; Kreil, D.; Nauser, T.; Kovalenko, M. (2016). "Detection of gamma photons using solution-grown single crystals of hybrid lead halide perovskites". Nature Photonics. 10 (9): 585–589. Bibcode:2016NaPho..10..585Y. doi:10.1038/nphoton.2016.139. hdl:20.500.11850/118934. S2CID 123312325.
^ a bBirowosuto, M. D. (16 November 2016). "X-ray Scintillation in Lead Halide Perovskite Crystals". Sci. Rep. 6: 37254. arXiv:1611.05862. Bibcode:2016NatSR...637254B. doi:10.1038/srep37254. PMC 5111063. PMID 27849019.
^ a b c d e fSaidaminov, Makhsud I.; Abdelhady, Ahmed L.; Murali, Banavoth; Alarousu, Erkki; Burlakov, Victor M.; Peng, Wei; Dursun, Ibrahim; Wang, Lingfei; He, Yao; MacUlan, Giacomo; Goriely, Alain; Wu, Tom; Mohammed, Omar F.; Bakr, Osman M. (2015). "High-quality bulk hybrid perovskite single crystals within minutes by inverse temperature crystallization". Nature Communications. 6: 7586. Bibcode:2015NatCo...6.7586S. doi:10.1038/ncomms8586. PMC 4544059. PMID 26145157.
^Cheetham, Anthony K.; Seshadri, Ram; Wudl, Fred (2022-06-30). "Chemical synthesis and materials discovery". Nature Synthesis. 1 (7): 514–520. arXiv:2207.07052. Bibcode:2022NatSy...1..514C. doi:10.1038/s44160-022-00096-3. ISSN 2731-0582. S2CID 250199748.
^Bakulin, A.A.; Selig, O.; Bakker, H.J.; Rezus, Y.L.A.; Muller, C.; Glaser, T.; Lovrincic, R.; Sun, Z.; Chen, Z.; Walsh, A.; Frost, J.M.; Jansen, T.L.C. (2015). "Real-Time Observation of Organic Cation Reorientation in Methylammonium Lead Iodide Perovskites" (PDF). J. Phys. Chem. Lett. 6 (18): 3663–3669. doi:10.1021/acs.jpclett.5b01555. hdl:10044/1/48952. PMID 26722739.
^Pisoni, Andrea; Jaćimović, Jaćim; Barišić, Osor S.; Spina, Massimo; Gaál, Richard; Forró, László; Horváth, Endre (2014). "Ultra-Low Thermal Conductivity in Organic–Inorganic Hybrid Perovskite CH3NH3PbI3". The Journal of Physical Chemistry Letters. 5 (14): 2488–2492. arXiv:1407.4931. doi:10.1021/jz5012109. PMID 26277821. S2CID 33371327.
^Juarez-Perez, Emilio J.; Hawash, Zafer; Raga, Sonia R.; Ono, Luis K.; Qi, Yabing (2016). "Thermal degradation of CH3NH3PbI3 perovskite into NH3 and CH3I gases observed by coupled thermogravimetry–mass spectrometry analysis". Energy Environ. Sci. 9 (11): 3406–3410. doi:10.1039/C6EE02016J. ISSN 1754-5692.
^Williams, Alice E.; Holliman, Peter J.; Carnie, Matthew J.; Davies, Matthew L.; Worsley, David A.; Watson, Trystan M. (2014). "Perovskite processing for photovoltaics: a spectro-thermal evaluation". J. Mater. Chem. A. 2 (45): 19338–19346. doi:10.1039/C4TA04725G. ISSN 2050-7488.
^Deschler, Felix; Price, Michael; Pathak, Sandeep; Klintberg, Lina E.; Jarausch, David-Dominik; Higler, Ruben; Hüttner, Sven; Leijtens, Tomas; Stranks, Samuel D.; Snaith, Henry J.; Atatüre, Mete; Phillips, Richard T.; Friend, Richard H. (2 April 2014). "High Photoluminescence Efficiency and Optically Pumped Lasing in Solution-Processed Mixed Halide Perovskite Semiconductors". The Journal of Physical Chemistry Letters. 5 (8): 1421–1426. doi:10.1021/jz5005285. PMID 26269988.
^Heo, Jin Hyuck; Song, Dae Ho; Han, Hye Ji; Kim, Seong Yeon; Kim, Jun Ho; Kim, Dasom; Shin, Hee Won; Ahn, Tae Kyu; Wolf, Christoph; Lee, Tae-Woo; Im, Sang Hyuk (2015). "Planar CH3NH3PbI3 Perovskite Solar Cells with Constant 17.2% Average Power Conversion Efficiency Irrespective of the Scan Rate". Advanced Materials. 27 (22): 3424–30. Bibcode:2015AdM....27.3424H. doi:10.1002/adma.201500048. PMID 25914242. S2CID 3165151.